Registros recuperados : 98 | |
3. | | MARINHO, N. P.; NISGOSKI, S.; BOLZON DE MUÑIZ, G. I. Avaliação das dimensões das fibras de colmos de bambu, Dendrocalamus giganteus (Wall) Munro, em diferentes idades. Ciência Florestal, Santa Maria, v. 24, n. 1, p. 251-256, jan./mar. 2014. Nota Técnica. Biblioteca(s): Embrapa Florestas. |
| |
4. | | FABROWSKI, F. J.; BOLZON de MUÑIZ, G. I.; KLOCK, U. Abordagem botânica das variedades populares da bracatinga (Mimosa scabrella, Bentahm). In: INTERNATIONAL CONGRESS AND EXHIBITION ON FOREST, 5., 1999, Curitiba. Forest 99: [resumos]. Rio de Janeiro: BIOSFERA, 1999. 1 CD-ROM. Autoria bilíngue: CONGRESSO E EXPOSICAO INTERNACIONAL SOBRE FLORESTAS, 5., 1999, Curitiba. Biblioteca(s): Embrapa Florestas. |
| |
5. | | BOLZON de MUNIZ, G. I.; BORSATO, R.; RENNER, R. Caracterização química e físico-mecânica da madeira da espécie miconiacinnamomifolia (de candole) Naudin, Floresta Ombrófila Densa. In: INTERNATIONAL CONGRESS AND EXHIBITION ON FOREST, 5., 1999, Curitiba. Forest 99: [resumos]. Rio de Janeiro: BIOSFERA, 1999. 1 CD-ROM. Autoria bilíngue: CONGRESSO E EXPOSICAO INTERNACIONAL SOBRE FLORESTAS, 5., 1999, Curitiba. Biblioteca(s): Embrapa Florestas. |
| |
13. | | MAGALHAES, W. L. E.; BOLZON de MUNIZ, G. I.; FABIS, M. H. M. Adsorção e dessorção de vapor d'água em madeira de Eucalyptus grandis Hill ex. Maiden revestida com stains, verniz e seladores. In: CONGRESSO BRASILEIRO DE INDUSTRIALIZAÇÃO DA MADEIRA E PRODUTOS DE BASE FLORESTAL, 1., 2004, Pinhais. Conferências, painéis, trabalhos convidados e pôsteres. [Curitiba]: IPEF, 2004. 6 p. Trabalho voluntário. Biblioteca(s): Embrapa Florestas. |
| |
17. | | MARINHO, N. P.; NISGOSKI, S.; KLOCK, U.; ANDRADE, A. S. de; BOLZON de MUÑIZ, G. I. Análise química do bambu-gigante (Dendrocalamus giganteus Wall. ex Munro) em diferentes idades. Ciência Florestal, Santa Maria, RS, v. 22, n. 2, p. 417-422, jul./set. 2012. Biblioteca(s): Embrapa Florestas. |
| |
18. | | FABROWSKI, F. J.; BOLZON de MUÑIZ, G. I.; KLOCK, U.; NAKASHIMA, T. Abordagem anatômica das variedades populares da bracatinga (Mimosa scabrella Bentham). In: INTERNATIONAL CONGRESS AND EXHIBITION ON FOREST, 5., 1999, Curitiba. Forest 99: [resumos]. Rio de Janeiro: BIOSFERA, 1999. 1 CD-ROM. Autoria bilíngue: CONGRESSO E EXPOSICAO INTERNACIONAL SOBRE FLORESTAS, 5., 1999, Curitiba. Biblioteca(s): Embrapa Florestas. |
| |
19. | | FARBOWSKI, F. J.; NAKASHIMA, T.; BOLZON de MUÑIZ, G. I.; KLOCK, U. Abordagem químico-qualitativa das variedade populares da bracatinga (Mimosa scabrella Bentahm). In: INTERNATIONAL CONGRESS AND EXHIBITION ON FOREST, 5., 1999, Curitiba. Forest 99: [resumos]. Rio de Janeiro: BIOSFERA, 1999. 1 CD-ROM. Autoria bilíngue: CONGRESSO E EXPOSICAO INTERNACIONAL SOBRE FLORESTAS, 5., 1999, Curitiba. Biblioteca(s): Embrapa Florestas. |
| |
Registros recuperados : 98 | |
|
|
| Acesso ao texto completo restrito à biblioteca da Embrapa Florestas. Para informações adicionais entre em contato com cnpf.biblioteca@embrapa.br. |
Registro Completo
Biblioteca(s): |
Embrapa Florestas. |
Data corrente: |
16/08/2016 |
Data da última atualização: |
11/07/2017 |
Tipo da produção científica: |
Artigo em Periódico Indexado |
Circulação/Nível: |
A - 2 |
Autoria: |
CADEMARTORI, P. H. G. de; CARVALHO, A. R. de; MARANGONI, P. R. D.; BERTON, M. A. C.; BLANCHET, P.; BOLZON DE MUNIZ, G. I.; MAGALHAES, W. L. E. |
Afiliação: |
PEDRO HENRIQUE GONZALEZ DE CADEMARTORI, Wood and Forestry Science Center (PPGEF), UFPR; AGNE ROANI DE CARVALHO, SENAI Institute of Innovation in Electrochemistry; PAULO ROBERTO DANTAS MARANGONI, SENAI Institute of Innovation in Electrochemistry; MARCOS ANTONIO COELHO BERTON, SENAI Institute of Innovation in Electrochemistry; PIERRE BLANCHET, Université Laval; GRACIELA INÊS BOLZON DE MUNIZ, UFPR; WASHINGTON LUIZ ESTEVES MAGALHAES, CNPF. |
Título: |
Adhesion performance and film formation of acrylic emulsion coating on mediumdensity fiberboard treated with Ar plasma. |
Ano de publicação: |
2016 |
Fonte/Imprenta: |
International Journal of Adhesion and Adhesives, v. 70, p. 322-328, Oct. 2016. |
DOI: |
10.1016/j.ijadhadh.2016.08.002 |
Idioma: |
Inglês |
Conteúdo: |
This work investigates the adhesion properties of medium density fiberboard (MDF) panel surfaces treated by an argon plasma at two power levels (50 and 150 W) and four glow discharge times (10, 40, 60 and 120 s) and then coated with an acrylic emulsion. Wettability parameters and film formation kinetics were investigated by water apparent contact angle and diffusing wave spectroscopy, respectively. Pull-off strength was used to determine coating/wood adhesion. The aging effect of 300-days in storage at ambient conditions was examined by apparent contact angle measurements. The wettability of the MDF surface was enhanced significantly - especially at the 150 W power level ? that improves coating/wood adhesion. A film formation process occurred in shorter time for plasma treated samples due to the faster motion of particles. MDF panels partially recovered their natural hydrophobicity in the first ten days of storage. Nevertheless, higher levels of power and time of glow discharge were able to slow down the aging effects. |
Palavras-Chave: |
Diffusing wave spectroscopy; Espectroscopia; MDF; Molhabilidade; Surface treatment; Tratamento da superfície. |
Thesagro: |
Madeira. |
Thesaurus NAL: |
Wettability. |
Categoria do assunto: |
W Química e Física |
Marc: |
LEADER 02002naa a2200301 a 4500 001 2051000 005 2017-07-11 008 2016 bl uuuu u00u1 u #d 024 7 $a10.1016/j.ijadhadh.2016.08.002$2DOI 100 1 $aCADEMARTORI, P. H. G. de 245 $aAdhesion performance and film formation of acrylic emulsion coating on mediumdensity fiberboard treated with Ar plasma.$h[electronic resource] 260 $c2016 520 $aThis work investigates the adhesion properties of medium density fiberboard (MDF) panel surfaces treated by an argon plasma at two power levels (50 and 150 W) and four glow discharge times (10, 40, 60 and 120 s) and then coated with an acrylic emulsion. Wettability parameters and film formation kinetics were investigated by water apparent contact angle and diffusing wave spectroscopy, respectively. Pull-off strength was used to determine coating/wood adhesion. The aging effect of 300-days in storage at ambient conditions was examined by apparent contact angle measurements. The wettability of the MDF surface was enhanced significantly - especially at the 150 W power level ? that improves coating/wood adhesion. A film formation process occurred in shorter time for plasma treated samples due to the faster motion of particles. MDF panels partially recovered their natural hydrophobicity in the first ten days of storage. Nevertheless, higher levels of power and time of glow discharge were able to slow down the aging effects. 650 $aWettability 650 $aMadeira 653 $aDiffusing wave spectroscopy 653 $aEspectroscopia 653 $aMDF 653 $aMolhabilidade 653 $aSurface treatment 653 $aTratamento da superfície 700 1 $aCARVALHO, A. R. de 700 1 $aMARANGONI, P. R. D. 700 1 $aBERTON, M. A. C. 700 1 $aBLANCHET, P. 700 1 $aBOLZON DE MUNIZ, G. I. 700 1 $aMAGALHAES, W. L. E. 773 $tInternational Journal of Adhesion and Adhesives$gv. 70, p. 322-328, Oct. 2016.
Download
Esconder MarcMostrar Marc Completo |
Registro original: |
Embrapa Florestas (CNPF) |
|
Biblioteca |
ID |
Origem |
Tipo/Formato |
Classificação |
Cutter |
Registro |
Volume |
Status |
Fechar
|
Nenhum registro encontrado para a expressão de busca informada. |
|
|