 | Acesso ao texto completo restrito à biblioteca da Embrapa Instrumentação. Para informações adicionais entre em contato com cnpdia.biblioteca@embrapa.br. |
|
Registro Completo |
|
Biblioteca(s): |
Embrapa Instrumentação. |
|
Data corrente: |
23/09/2021 |
|
Data da última atualização: |
10/06/2022 |
|
Tipo da produção científica: |
Artigo em Periódico Indexado |
|
Autoria: |
SILVA, D. W.; BUFALINO, L.; MARTINS, M. A.; SAVASTANO JÚNIOR, H.; TONOLI, G. H. D.; MENDES, L. M. |
|
Afiliação: |
MARIA ALICE MARTINS, CNPDIA. |
|
Título: |
Superabsorbent ability polymer to reduce the bulk density of extruded cement boards. |
|
Ano de publicação: |
2021 |
|
Fonte/Imprenta: |
Journal of Building Engineering, v. 43, 103130, 2021. |
|
Páginas: |
1 - 7 |
|
ISSN: |
2352-7102 |
|
DOI: |
https://doi.org/10.1016/j.jobe.2021.103130 |
|
Idioma: |
Inglês |
|
Conteúdo: |
The extrusion process has numerous advantages in the production of cement materials; however, cement extruded products over gain bulk density, adding costs to their fixation, workability, and application as structural reinforcement. The objective of this research was to develop and test extruded lightweight cement-based boards with the addition of superabsorbent polymer (SAP). A plain cement board containing 70% of cement and 30% of limestone filler was prepared. The different percentages of SAP from 0.0 to 2.0% based on cement mass did not interfere in the extrusion process. However, an expansion of the cement boards containing 1.0, 1.5, and 2.0% SAP occurred when passing through the extruder nozzle. The apparent porosity increased, and millimetric voids arose in the cement boards by increasing the SAP percentage. The apparent density of the cement boards favorably decreased from 8.6 to 28.4% by adding different percentages of SAP. However, the microstructural modifications raised the water absorption and substantially decreased the mechanical performance. Still, adding only 0.5% of SAP reduced the bulk density by about 10% without substantially decreasing the mechanical performance of the cement boards. Therefore, the SAP was very efficient in producing lightweight cement boards by extrusion. |
|
Palavras-Chave: |
Air-entraining; Cement materials. |
|
Categoria do assunto: |
-- |
|
Marc: |
LEADER 02035naa a2200241 a 4500
001 2134735
005 2022-06-10
008 2021 bl uuuu u00u1 u #d
022 $a2352-7102
024 7 $ahttps://doi.org/10.1016/j.jobe.2021.103130$2DOI
100 1 $aSILVA, D. W.
245 $aSuperabsorbent ability polymer to reduce the bulk density of extruded cement boards.$h[electronic resource]
260 $c2021
300 $a1 - 7
520 $aThe extrusion process has numerous advantages in the production of cement materials; however, cement extruded products over gain bulk density, adding costs to their fixation, workability, and application as structural reinforcement. The objective of this research was to develop and test extruded lightweight cement-based boards with the addition of superabsorbent polymer (SAP). A plain cement board containing 70% of cement and 30% of limestone filler was prepared. The different percentages of SAP from 0.0 to 2.0% based on cement mass did not interfere in the extrusion process. However, an expansion of the cement boards containing 1.0, 1.5, and 2.0% SAP occurred when passing through the extruder nozzle. The apparent porosity increased, and millimetric voids arose in the cement boards by increasing the SAP percentage. The apparent density of the cement boards favorably decreased from 8.6 to 28.4% by adding different percentages of SAP. However, the microstructural modifications raised the water absorption and substantially decreased the mechanical performance. Still, adding only 0.5% of SAP reduced the bulk density by about 10% without substantially decreasing the mechanical performance of the cement boards. Therefore, the SAP was very efficient in producing lightweight cement boards by extrusion.
653 $aAir-entraining
653 $aCement materials
700 1 $aBUFALINO, L.
700 1 $aMARTINS, M. A.
700 1 $aSAVASTANO JÚNIOR, H.
700 1 $aTONOLI, G. H. D.
700 1 $aMENDES, L. M.
773 $tJournal of Building Engineering$gv. 43, 103130, 2021.
Download
Esconder MarcMostrar Marc Completo |
|
Registro original: |
Embrapa Instrumentação (CNPDIA) |
|
|
Biblioteca |
ID |
Origem |
Tipo/Formato |
Classificação |
Cutter |
Registro |
Volume |
Status |
URL |
Voltar
|
|
|
| Registros recuperados : 5 | |
| 2. |  | BORDUCHI, L. C. L.; MILORI, D. M. B. P.; MEYER, M. C.; VILLAS BOAS, P. R. Quantificação nutricional foliar usando a espectroscopia de emissão de plasma induzido por laser. In: BASSOI, L. H.; BERNARDI, A. C. de C.; VAZ, C. M. P.; PIRES, J. L. F.; GEBLER, L.; JORGE, L. A. de C.; INAMASU, R. Y. (ed.). Agricultura de Precisão: Um Novo Olhar na Era Digital. São Carlos, SP: Editora Cubo, 2024. cap. 23. 234-238| Tipo: Capítulo em Livro Técnico-Científico |
| Biblioteca(s): Embrapa Instrumentação; Embrapa Soja. |
|    |
| 5. | | RANULFI, A. C.; SENESI, G. S.; CAETANO, J. B.; MEYER, M. C.; MAGALHÃES, A. B.; BOAS, P. R. V.; MILORI, D. M. B. P. Nutritional characterization of healthy and Aphelenchoides besseyi infected soybean leaves by laser-induced breakdown spectroscopy (LIBS). Microchemical Journal, v. 141, p. 118-126, 2018.| Tipo: Artigo em Periódico Indexado | Circulação/Nível: A - 1 |
| Biblioteca(s): Embrapa Soja. |
|  |
| Registros recuperados : 5 | |
|
| Nenhum registro encontrado para a expressão de busca informada. |
|
|