| Registros recuperados : 1 | |
| 1. |  | TABALDI, L. A.; RUPPENTHAL, R.; PEREIRA, L. B.; CARGNELUTTI, D.; GONÇALVES, J. F.; MORSCH, V. M.; SCHETINGER, M. R. C. Presence of multiple acid phosphatases activity in seedlings os cucumber, radish and rocket salad. Ciência Rural, Santa Maria, v. 38, n. 3, p. 650-657, jun. 2008.| Biblioteca(s): Embrapa Hortaliças. |
|    |
| Registros recuperados : 1 | |
|
|
|
 | Acesso ao texto completo restrito à biblioteca da Embrapa Instrumentação. Para informações adicionais entre em contato com cnpdia.biblioteca@embrapa.br. |
Registro Completo
|
Biblioteca(s): |
Embrapa Instrumentação. |
|
Data corrente: |
22/12/1999 |
|
Data da última atualização: |
22/12/1999 |
|
Autoria: |
ASSIS, O. B. G.; CRNKOVIC, F. C.; MACHADO, R.; AVACA, L. A.; FERRANTE, M.; MACHADO, S. A. S. |
|
Afiliação: |
EMBRAPA-CNPDIA; USP-IQSC-GMEME; UFSCar-CCDM; UFSCar-DEMa. |
|
Título: |
Powder metallurgy processing of Ni-Co base electrodes for application in water electrolysis. |
|
Ano de publicação: |
1997 |
|
Fonte/Imprenta: |
In: INTERNATIONAL LATIN-AMERICAN CONFERENCE ON POWDER TECHNOLOGY=CONFERENCIA INTERNACIONAL LATINO-AMERICANA EM TECNOLOGIA DO PO, 1., Nov. 1997, Aguas de Lindoia, SP. Information/Informativo... Aguas de Lindoia: Associacao Brasileira de Ceramica, 1997. |
|
Páginas: |
não paginado. |
|
Idioma: |
Inglês |
|
Conteúdo: |
Electrodes of Co, Ni and Ni50Co50 were produced by pwder metallurgy techniques aaiming at their application as cathodes for water electrolyssis system. Sintering was carried out in vacuum/argon atmosphere at low temperature in order to enhance surface electroactivity by an increase if the geometric area. The Ni-Co alloyng was obtained by mechanical synthesis, making use of the appropriated route. The final electrodes presented porosity of around 12% where the electrochemical tests presented increasing in the critical peak when compared with eletroplated flat samples. |
|
Palavras-Chave: |
Mechanical alloying; Sintering; Water electrolysis. |
|
Thesaurus NAL: |
electrochemistry. |
|
Categoria do assunto: |
-- |
|
Marc: |
LEADER 01455naa a2200241 a 4500
001 1027136
005 1999-12-22
008 1997 bl --- 0-- u #d
100 1 $aASSIS, O. B. G.
245 $aPowder metallurgy processing of Ni-Co base electrodes for application in water electrolysis.
260 $c1997
300 $anão paginado.
520 $aElectrodes of Co, Ni and Ni50Co50 were produced by pwder metallurgy techniques aaiming at their application as cathodes for water electrolyssis system. Sintering was carried out in vacuum/argon atmosphere at low temperature in order to enhance surface electroactivity by an increase if the geometric area. The Ni-Co alloyng was obtained by mechanical synthesis, making use of the appropriated route. The final electrodes presented porosity of around 12% where the electrochemical tests presented increasing in the critical peak when compared with eletroplated flat samples.
650 $aelectrochemistry
653 $aMechanical alloying
653 $aSintering
653 $aWater electrolysis
700 1 $aCRNKOVIC, F. C.
700 1 $aMACHADO, R.
700 1 $aAVACA, L. A.
700 1 $aFERRANTE, M.
700 1 $aMACHADO, S. A. S.
773 $tIn: INTERNATIONAL LATIN-AMERICAN CONFERENCE ON POWDER TECHNOLOGY=CONFERENCIA INTERNACIONAL LATINO-AMERICANA EM TECNOLOGIA DO PO, 1., Nov. 1997, Aguas de Lindoia, SP. Information/Informativo... Aguas de Lindoia: Associacao Brasileira de Ceramica, 1997.
Download
Esconder MarcMostrar Marc Completo |
|
Registro original: |
Embrapa Instrumentação (CNPDIA) |
|
|
Biblioteca |
ID |
Origem |
Tipo/Formato |
Classificação |
Cutter |
Registro |
Volume |
Status |
Fechar
|
| Nenhum registro encontrado para a expressão de busca informada. |
|
|