Autoria: |
SILVA, D. W.; SCATOLINO, M. V.; PEREIRA, T. G. T.; VILELA, A. P.; EUGENIO, T. M. C.; MARTINS, M. A.; MENDES, R. F.; BUFALINO, L.; TONOLI, G. H. D.; MENDES, L. M. |
|
Afiliação: |
MARIA ALICE MARTINS, CNPDIA. |
|
Título: |
Influence of thermal treatment of eucalyptus fibers on the physical-mechanical properties of extruded fiber-cement composites. |
|
Ano de publicação: |
2020 |
|
Fonte/Imprenta: |
Materials Today: Proceedings, v. 31, 2020. |
|
Páginas: |
S348-S352 |
|
ISSN: |
2214-7853 |
|
DOI: |
https://doi.org/10.1016/j.matpr.2020.04.764 |
|
Idioma: |
Inglês |
|
Conteúdo: |
This study proposes to evaluate the effect of the heat treatment in commercial eucalyptus fibers (produced by thermo-mechanical process) on the physical-mechanical properties of extruded fiber-cements composites. The fibers were treated with different temperatures of heat treatment (140, 170, 200 and 230 °C) for 60 min in a “Macro-ATG” oven. The chemical and morphological characteristics of the natural fibers were evaluated before and after the thermal treatment. The cementitious paste was composed by 67.9% cement, 29.1% limestone and 3% eucalyptus fibers. Hydroxypropylmethylcellulose (HPMC) and polyether carboxylic acid (ADVA 175) were added to the cement paste both in 1% (based on the cement mass) to facilitate the extrusion process. The thermal treatments at 200 and 230 °C were efficient in reducing the extractives content. On the other hand, a decrease in length, diameter and lumen size of the fibers has occurred. The decrease in extractives content did not influence the properties of water absorption, modulus of rupture (MOR) and modulus of elasticity (MOE). The increase in lignin content resulted in increase for apparent porosity and decrease of the toughness in reinforced fiber-cement produced with fibers treated at 200 and 230 °C. The application of the thermal treatment for the fibers did not show improvement in fiber-cement in the evaluated conditions. It is recommended to evaluate other properties of the fiber-cement reinforced with the mentioned treated fibers, such as natural and laboratorial weathering. MenosThis study proposes to evaluate the effect of the heat treatment in commercial eucalyptus fibers (produced by thermo-mechanical process) on the physical-mechanical properties of extruded fiber-cements composites. The fibers were treated with different temperatures of heat treatment (140, 170, 200 and 230 °C) for 60 min in a “Macro-ATG” oven. The chemical and morphological characteristics of the natural fibers were evaluated before and after the thermal treatment. The cementitious paste was composed by 67.9% cement, 29.1% limestone and 3% eucalyptus fibers. Hydroxypropylmethylcellulose (HPMC) and polyether carboxylic acid (ADVA 175) were added to the cement paste both in 1% (based on the cement mass) to facilitate the extrusion process. The thermal treatments at 200 and 230 °C were efficient in reducing the extractives content. On the other hand, a decrease in length, diameter and lumen size of the fibers has occurred. The decrease in extractives content did not influence the properties of water absorption, modulus of rupture (MOR) and modulus of elasticity (MOE). The increase in lignin content resulted in increase for apparent porosity and decrease of the toughness in reinforced fiber-cement produced with fibers treated at 200 and 230 °C. The application of the thermal treatment for the fibers did not show improvement in fiber-cement in the evaluated conditions. It is recommended to evaluate other properties of the fiber-cement reinforced with the mentioned treated fibers, s... Mostrar Tudo |
|
Palavras-Chave: |
Cementitious composites; Chemical characterization; Extruded process; Morphological characterization. |
|
Categoria do assunto: |
-- |
|
Marc: |
LEADER 02534naa a2200313 a 4500
001 2124283
005 2022-08-16
008 2020 bl uuuu u00u1 u #d
022 $a2214-7853
024 7 $ahttps://doi.org/10.1016/j.matpr.2020.04.764$2DOI
100 1 $aSILVA, D. W.
245 $aInfluence of thermal treatment of eucalyptus fibers on the physical-mechanical properties of extruded fiber-cement composites.$h[electronic resource]
260 $c2020
300 $aS348-S352
520 $aThis study proposes to evaluate the effect of the heat treatment in commercial eucalyptus fibers (produced by thermo-mechanical process) on the physical-mechanical properties of extruded fiber-cements composites. The fibers were treated with different temperatures of heat treatment (140, 170, 200 and 230 °C) for 60 min in a “Macro-ATG” oven. The chemical and morphological characteristics of the natural fibers were evaluated before and after the thermal treatment. The cementitious paste was composed by 67.9% cement, 29.1% limestone and 3% eucalyptus fibers. Hydroxypropylmethylcellulose (HPMC) and polyether carboxylic acid (ADVA 175) were added to the cement paste both in 1% (based on the cement mass) to facilitate the extrusion process. The thermal treatments at 200 and 230 °C were efficient in reducing the extractives content. On the other hand, a decrease in length, diameter and lumen size of the fibers has occurred. The decrease in extractives content did not influence the properties of water absorption, modulus of rupture (MOR) and modulus of elasticity (MOE). The increase in lignin content resulted in increase for apparent porosity and decrease of the toughness in reinforced fiber-cement produced with fibers treated at 200 and 230 °C. The application of the thermal treatment for the fibers did not show improvement in fiber-cement in the evaluated conditions. It is recommended to evaluate other properties of the fiber-cement reinforced with the mentioned treated fibers, such as natural and laboratorial weathering.
653 $aCementitious composites
653 $aChemical characterization
653 $aExtruded process
653 $aMorphological characterization
700 1 $aSCATOLINO, M. V.
700 1 $aPEREIRA, T. G. T.
700 1 $aVILELA, A. P.
700 1 $aEUGENIO, T. M. C.
700 1 $aMARTINS, M. A.
700 1 $aMENDES, R. F.
700 1 $aBUFALINO, L.
700 1 $aTONOLI, G. H. D.
700 1 $aMENDES, L. M.
773 $tMaterials Today: Proceedings$gv. 31, 2020.
Download
Esconder MarcMostrar Marc Completo |
|
Registro original: |
Embrapa Instrumentação (CNPDIA) |
|
|
Biblioteca |
ID |
Origem |
Tipo/Formato |
Classificação |
Cutter |
Registro |
Volume |
Status |
URL |
Voltar
|
|
|
| Registros recuperados : 11 | |
| 3. |  | MASCARENHAS, A. R. P.; SCATOLINO, M. V.; DIAS, M. C.; MARTINS, M. A.; MELO, R. R. de; MENDONDÇA, M. C.; TONOLI, G. H. D. Association of cellulose micro/nanofibrils and silicates for cardboard coating: Technological aspects for packaging. Industrial Crops & Products, v. 188, e115667, 2022.| Tipo: Artigo em Periódico Indexado | Circulação/Nível: A - 1 |
| Biblioteca(s): Embrapa Instrumentação. |
|    |
| 4. | | GUIMARÃES, B. M. R.; SCATOLINO, M. V.; MARTINS, M. A.; FERREIRA, S. R.; MENDES, L. M.; LIMA, J. T.; GUIMARÃES JUNIOR, M.; TONOLI, G. H. D. Bio-based films/nanopapers from lignocellulosic wastes for production of added-value micro-/nanomaterials. Environmental Science and Pollution Research, v. 29, 2022. 8665-8683| Tipo: Artigo em Periódico Indexado | Circulação/Nível: A - 1 |
| Biblioteca(s): Embrapa Instrumentação. |
| |
| 5. | | SCATOLINO, M. V.; FONSECA, C. S.; GOMES, M. da S.; ROMPA, V. D.; MARTINS, M. A.; TONOLI, G. H. D.; MENDES, L. M. How the surface wettability and modulus of elasticity of the Amazonian paricá nanofibrils films are affected by the chemical changes of the natural fibers. European Journal of Wood and Wood Products, v. 76, n. 6, 2018. p. 1581-1594| Tipo: Artigo em Periódico Indexado | Circulação/Nível: B - 1 |
| Biblioteca(s): Embrapa Instrumentação. |
| |
| 6. | | MASCARENHAS, A. R. P.; SCATOLINO, M. V.; DIAS, M. C.; MARTINS, M. A.; MELO, R. R. de; DAMÁSIO, R. A. P.; MENDONÇA, M. C.; TONOLI, G. H. D. Fibers pre-treatments with sodium silicate afect the properties of suspensions, flms, and quality index of cellulose micro/nanofbrils. Nordic Pulp & Paper Research Journal, v. 37, n. 3, 2022. 534-552| Tipo: Artigo em Periódico Indexado | Circulação/Nível: A - 2 |
| Biblioteca(s): Embrapa Instrumentação. |
| |
| 8. | | SILVA, D. W.; SCATOLINO, M. V.; PEREIRA, T. G. T.; VILELA, A. P.; EUGENIO, T. M. C.; MARTINS, M. A.; MENDES, R. F.; BUFALINO, L.; TONOLI, G. H. D.; MENDES, L. M. Influence of thermal treatment of eucalyptus fibers on the physical-mechanical properties of extruded fiber-cement composites. Materials Today: Proceedings, v. 31, 2020. S348-S352| Tipo: Artigo em Periódico Indexado | Circulação/Nível: B - 4 |
| Biblioteca(s): Embrapa Instrumentação. |
| |
| 9. | | DIAS, M. C.; ZIDANES, U. L.; MASCARENHAS, A. R. P.; SETTER, C.; SCATOLINO, M. V.; MARTINS, M. A.; MORI, F. A.; BELGACEM, M. N.; TONOLI, G. H. D.; FERREIRA, S. R. Mandacaru cactus as a source of nanofibrillated cellulose for nanopaper production. International Journal of Biological Macromolecules, v. 235, 123850, 2023. 1-11| Tipo: Artigo em Periódico Indexado | Circulação/Nível: A - 1 |
| Biblioteca(s): Embrapa Instrumentação. |
| |
| 10. | | SCATOLINO, M. V.; DIAS, M. C.; SILVA, D. W.; BUFALINO, L.; MARTINS, M. A.; PICCOLI, R. H.; TONOLI, G. H. D.; LONDERO, A. A.; OENNING NETO, V.; MENDES, L. M. Tannin-stabilized silver nanoparticles and citric acid added associated to cellulose nanofibrils: effect on film antimicrobial properties. SN Applied Science, n. 1, art. 1243, 2019 Published online: 20 September 2019.| Tipo: Artigo em Periódico Indexado |
| Biblioteca(s): Embrapa Instrumentação. |
| |
| 11. | | SANTOS, M. E. C. DOS; MELO, R. R. DE; CORREIA, D.; SOUSA, J. A. de; SANTOS, A. M.; SILVA, A. K. V. DA; PAULA, E. A. DE O.; ALVES, A. R.; SCATOLINO, M. V.; RUSCH, F.; MASCARENHAS, A. R. P.; PIMENTA, A. S.; STANGERLIN, D. M. Variation in the Basic Density of Woods Produced in the Brazilian Semiarid Region Subjected to Different Irrigation Regimes. Forests, 14, 2168, 2023.| Tipo: Artigo em Periódico Indexado | Circulação/Nível: A - 2 |
| Biblioteca(s): Embrapa Agroindústria Tropical; Embrapa Florestas. |
|  |
| Registros recuperados : 11 | |
|
| Nenhum registro encontrado para a expressão de busca informada. |
|
|